Spectrum® 3D PLA WOOD Filament 1.75mm 0.5kg Spool

Spectrum PLA Wood Filament

Have you ever wished you could print a model that looks and feels like real wood? Then we offer you the perfect solution. The Spectrum PLA Wood Filaments are easy to process and create a model that not only looks like wood, but also fills like wood and even smells like wood during production. What's more, after printing, the material can be processed just as you would with wood. With Spectrum PLA Wood filaments, you can dive into a new world of 3D printing. 

3D printing from natural wood

If you are now wondering how a filament can not only feel like this, but also look like this, this question is quickly answered. Spectrum PLA Wood Filament is made from pure PLA that is mixed with natural wood particles. This gives you a 100% organic and biological product that is completely degradable. The wood fibers do not influence the properties of the PLA material, but complement them positively. The special thing about using Spectrum PLA Wood Filaments is the specific wood smell that is created during the printing process.

A combination of plastic with natural materials

The Spectrum PLA Wood material is something very special. By combining plastic with the natural wood fibers, you can process your models like real wood after they cool down. The chipboard-like structure can be painted or mechanically processed (sawn, sanded). Please note, since the product contains natural wood, there may be slight color variations as in nature.

Fields of application:

• Printing of elements that provide both good thermal insulation and very high moisture resistance.
• educational projects
• advertising material
• decorative art
• interior design

Technical data:

• Brand: Spectrum
• Material: PLA (Polylactic Acid) + gemahlene Holzpartikel
• Wire thickness: 1,75 mm
• Dimensional accuracy: + / - 0.03 mm
• Content / Weight: 0,5 kg
• Length: ca. 180,85 m
• Recommended print temperature: 190 - 220 °C
• Recommended print bed temperature: 0 - 45 °C
• Suggested printing speed: 20 - 50 mm/s
• Material density: 1.19 g/cm3
• Melt flow index (MFR): 2.5-5.0 g / 10 min

• Melt temperature: > 155°C
• Impact strength unnotched at +23°C: 21 kJ/m2
• Impact strength not notched at +23°C: 4.4 kJ/m2
• Tensile elongation: 0,05
• Tensile strength: 38 MPa
• modulus of elasticity: 2900 MPa
• Active fan: Yes
• Layer height: 0.05 - 0.30 mm
• Shell thickness: 0.40 – 2.70 mm
• Closed construction space: not necessary
• Drying box: not necessary
• Ruby or hardened nozzle: not necessary
• Recommended nozzle? 0.4 mm